Olie- en vernisfabriek Vliegenthart BV

Grondstoffen

[metaslider id=1210]


Overzicht grondstoffen

Castorolie

  • Standolie
  • Gepolymeriseerd
  • Gedehydrateerd
  • Gehydrogeneerd

Lijnolie

  • Standolie
  • Gekookt
  • Dubbelgekookt
  • Geraffineerd
  • Geoxideerd
  • Wateremulgeerbaar
  • Ruwe lijnolie

Raapolie

  • Standolie
  • Geraffineerd
  • Geoxideerd
  • Wateremulgeerbaar

Saffloerolie

  • Standolie

Tung-olie

  • Standolie

Sojaolie

  • Standolie
  • Geraffineerd
  • Geoxideerd
  • Wateremulgeerbaar
  • Lecithine

Siccatieven

  • Bariumoctoaat
  • Calciumoctoaat
  • Cobaltoctoaat
  • Cobaltneodececanoaat
  • Koperoctoaat
  • Mangaanoctoaat
  • Kaliumoctoaat
  • Strontium
  • Zink
  • Zirkoniumoctoaat
  • Mengsiccatieven
  • Cobalt alternatieven

Klik op de productgroep om direct naar de technische gegevens te gaan.


Technische gegevens

Plantaardige oliën

Castorolie

Technische gegevens


Technische gegevens


Technische gegevens


Technische gegevens


Lijnolie


Type: Lijnolie standolie is een gepolymeriseerde, geraffineerde lijnolie.
Eigenschappen: Lijnolie standolie is zoals alle lijnoliën een vergelende olie. Dit wordt veroorzaakt door het hoge gehalte onverzadigde verbindingen in lijnolie. Lijnolie standolie kan op elke gewenste viscositeit worden gebracht, dit maakt het mogelijk dat wij lijnolie standolie kunnen leveren in de viscositeiten 30, 45, 90, 120, 250 en 450 P, 20°C. De kleur is zeer blank. (Speciale viscositeiten kunnen op aanvraag ook geproduceerd worden.)
Toepassing: Lijnolie standolie kan vermengd worden met alkydharsen om elastischer en beter glanzende verven te verkrijgen. Het is zeer geschikt voor het “opvetten” van gekleurde verfsystemen. Tevens wordt het veel gebruikt als toevoeging bij de productie van butyleen-kitten en als oliebestanddeel voor beitssystemen.
Verwerking: Bijmengen naar behoefte in Uw bestaande recepten.


Type: Gekookte lijnolie is een zuivere, rauwe lijnolie die verhit wordt en waar na toevoeging van een katalysator lucht wordt doorgeleid.
Eigenschappen: Gekookte lijnolie is helder en is een zeer sneldrogende olie.
Toepassing: Vanwege de drogende eigenschappen uitstekend geschikt voor de fabricage van verf en/of kitten of voor het “opvetten” van beitsen. Tevens is gekookte llijnolie bij uitstek geschikt als houtverduurzamingsmiddel en als middel om ijzer tegen roest te beschermen. Voor de laatste applicatie is het zelfs aan te  bevelen om metaal te behandelen dat al iets roestig is.
Verwerking: Bijmengen naar behoefte in Uw bestaande recepten. Indien gebruikt als houtverduurzamingsmiddel of anti-roestmiddel ruim met de kwast opbrengen.


Technische gegevens


Type: Geraffineerde lijnolie wordt bereid door rauwe lijnolie te vermengen met het natuur-product bleekaarde en dit dan te verwarmen. Bleekaarde is een fossiele kaolienklei (montmorilloniet) die zeer poreus van structuur is, waardoor slijmstoffen en kleurstoffen uit de rauwe lijnolie in de bleekaarde geabsorbeerd worden. De lijnolie /  bleekaarde wordt gefiltreerd en men houdt een schitterend heldere lijnolie over, die zeer blank van kleur is.
Eigenschappen: Geraffineerde lijnolie heeft de neiging te vergelen in witte en pastelkleurige verven. Dit wordt veroorzaakt door het hoge gehalte onverzadigde verbindingen in lijnolie.
Toepassing: De hoge zuiverheid van geraffineerde lijnolie maakt deze veel gevraagd door kunstschilders en tot een hoogwaardige grondstof voor de fabricage van alkydhars. Het wordt ook toegepast in de verf- en drukinktproductie en in de chemische industrie.
Verwerking:


Technische gegevens


Type: Water emulgeerbare lijnolie is een zuivere, rauwe lijnolie die op een speciale wijze wordt behandeld, zonder toevoeging van emulgatoren.
Eigenschappen: Afhankelijk van de gewenste viscositeit is deze olie licht tot donker van kleur. Deze olie kan gemakkelijk met normaal water worden geëmulgeerd. Na droging van deze emulsie blijft er een blanke film over.
Toepassing: Als toevoeging te gebruiken bij watergedragen alkyd-verfsystemen om meer olie-karakter te verkrijgen. Tevens kan deze olie worden toegepast bij de productie van watergedragen alkyd-beitssystemen.
Verwerking: Bijmengen naar behoefte in Uw bestaande recepten.

Volgt


Terug naar het overzicht

Raapolie


Technische gegevens


Type: Een geraffineerde ruwe raapolie, waarbij de raffinage de kleur en de reuk verbetert. In deze geraffineerde raapolie is géén restproduct meer aanwezig.
Eigenschappen: Een niet-drogende olie die helder van kleur is.
Toepassing: Vanwege de niet-drogende eigenschappen uitstekend geschikt voor gebruik in smeermiddelen. Daarnaast kan het ook gebruikt worden als koelolie en voor andere technische toepassingen. Deze geraffineerde raapolie is ook geschikt als eetbare olie. Echter, opslag, Transport en verpakking dienen dan wel te voldoen aan de eisen voor de voedsel industrie.


Technische gegevens


Technische gegevens


Terug naar het overzicht

Sojaolie


Technische gegevens


Technische gegevens


Technische gegevens


Technische gegevens


Type: LVLEC 70 is een technische, ongebleekte soja  lecithine. De lecithine-componenten, zoals o.a. fosfatidylethanolamine, fosfatidylcholine, fosfati dylinositol komen voor in verhoudingen, zoals ook in de sojabonen het geval is.
Eigenschappen: LVLEC 70 is oplosbaar in alcohol, chloroform en ether. Het is onoplosbaar in water.
Toepassing: LVLEC 70 wordt graag toegepast als maalhulpmiddel, d.w.z. als toevoeging tijdens het dispergeren van de pigmenten in het bindmiddel. LVLEC 70 bevordert sterk de vorming van een emulsie en verbetert de viscositeit. LVLEC 70 heeft een sterk pigment benattend vermogen.


Terug naar het overzicht

Andere oliën


Technische gegevens


Technische gegevens


Terug naar het overzicht

Diversen


Type: Gomhars is een mengsel van vrije harszuren, afkomstig van de balsem van enkele soorten naaldbomen.
Eigenschappen: Geelachtig tot lichtbruine glasachtige stukken. Gomhars is vast en broos bij kamertemperatuur, maar wordt snel zacht bij het verwarmen, wordt kleverig bij handwarmte. Langzaam oplosbaar in alcohol of azijnzuur, volledig oplosbaar in ether en chloroform en waneer het verwarmd wordt organische oplosmiddelen.
Toepassing: In de verf- en lakindustrie voor de productie van o.a. natuurverven, papierlijm en aniti fauling verven.
Verwerking: Bijmengen na behoefte in uw bestaande recepten.


Technische gegevens


Type: Gomterpentijn is een etherische olie die wordt verkregen uit de balsem (wondvocht) van pijnbomen.
Eigenschappen: Zuivere gomterpentijn is helder en kleurloos, heeft een groot oplossend vermogen en versnelt de oxydatieve droging van olieverven.
Toepassing: Uitstekend geschikt als verdunningsmiddel/oplosmiddel voor verven op basis van natuurlijke oliën.
Verwerking: Bijmengen na behoefte in Uw bestaande recepten.


Technische gegevens


Terug naar het overzicht

Siccatieven – enkelvoudige metalen


This drier is used as substitute for lead in lead free paints. Barium improves the through-dying of a coating and has good pigments and wetting properties. Unlike, lead, barium is not thought to be a cumulative poison, but it has quite a high acute toxicity which may preclude its use in certain systems. They are less moisture sensitive and unlike lead does not cause haze in alkyds.


Calcium is one of the most important auxiliary drier. It has little drying action in itself but is very useful in combination with active driers. Calcium has strong surface active properties; hence it is very effective as a dispersing agent. It also helps to certain extent as an anti-adsorption agent to prevent loss of drier on storage. In vehicles that show poor tolerance for lead, it is possible to replace part of the lead with a larger amount use of calcium to prevent precipitation haziness or turbidity of lead phthalate observed in compositions containing dibasic acids, like phthalic anhydride.

Excess use of calcium should be normally avoided as it can affect the rheological properties due to its surface activity and possibility of incorporation of more quantity of the acidic radical. Calcium Improves hardness and gloss, as well as reduces skinning and silking.


Cobalt is one of the most efficient highly potent and effective drier per unit of metal known today. It is primarily an oxidation and as such acts as a ‘Surface’ or ‘Top Drier:

Cobalt provides fastest surface drying properties and is required to be used in small quantities.

Used alone, it may have a tendency to cause surface wrinkling and poor through – dry. Therefore, to provide uniform drying, cobalt is generally used in combination with other metals, such as manganese, zirconium, lead, calcium and combinations of these metals. Excess use of cobalt may result in premature skin formation. This can prevent further passage of oxygen and then reduce the efficiency of drying, ultimately resulting in formation of soft films.


Technische gegevens


Technische gegevens


Terug naar het overzicht


Manganese is also an active drier, though generally less active than cobalt. As an accelerator of polymerization in banking finishes, it is usually more effective than cobalt. Manganese gives better low temperature drying performance than cobalt, and films containing manganese do not suffer from wrinkling under high – humidity conditions. It is generally preferred to formulate white enamels with no manganese or from low manganese content; a pink or pink- yellow colour develops of high – manganese contents are used.

Manganese has anti-bloom properties and gives hard, water resistant films. Manganese drier activity seems less sensitive to temperature changes than does cobalt. Manganese also has the advantage that it does not cause baked films to embrittle. Additionally, in systems prone to skinning, such as urethane oils, manganese cab be used with good results.

Excess use of manganese leads to premature breakdown of the films and discolour the paint film.

Technische gegevens


Technische gegevens


Through an auxiliary drier, zinc has negative catalytic activity. Zinc basically keeps the films open by controlling the activity of cobalt. It thus helps uniforms drying and results in hard films. It also eliminates wrinkling in air drying systems and frosting and gas checking in stoving finished. It also eliminates discolouration caused by complexing of other metal driers and helps to stabilize lead, promote film hardness and improve gloss and colour retention of enamels.

Zinc is a powerful wetting and dispersing agent, and when incorporated early in the formulation, it greatly reduces the time of mixing and grinding.

The amount of zinc required for mono-molecular coverage varies with different pigments ranging from 1.0 to 1.5 percent for blacks, blues, reds and approx.O.5 percent of the remaining pigments.


Zirconium is an important through drier, most widely accepted as replacement for lead drier. Zirconium improves through drying mainly by the formation of co-ordination bonds. Zirconium drier does not undergo any noticeable change even in the presence of strong oxidising catalyst and does not readily precipitate and disrupt gloss. Zirconium shows less tendency to yellow and better durability compared to other auxiliary driers. It often results in more flexible films than lead drier. Zirconium drier does not destroy the luster of aluminum pigmentation, nor does it sulfide stain. It is used mainly with cobalt and calcium: Generally one third unit of the quantity of Zirconium would replace one unit of lead based on metal. The pigment wetting and dispersing property of Zirconium is relatively less than lead drier.


Terug naar het overzicht

Andere siccatieven


Type: Een droger voor oxidatief drogende bindmiddelen opgelost in white spirit high flash.
Eigenschappen: Naast cobalt en zirconium of lood de meest actieve droger. Mangaan bevordert zowel de door-droging als de oppervlakte-droging. De drogingeigenschappen liggen tussen die van cobalt en zirconium of lood.
Toepassing: Wordt vooral gebruikt in combinatie met cobalt en zirconium of lood in gekleurde verfsystemen. Lichte verfsystemen kunnen gemakkelijk geel kleuren vanwege de bruine kleur van mangaan.
Verwerking: Dosering: 0,03 – 0,06% Mn Metaal op vast bindmiddel. Dit kan bereikt worden door 0,03 – 0,06 kg Mangaan 10% Mn aan 100 kg vast bindmiddel toe te voegen.


Technische gegevens Drier 410

Technische gegevens Drier 420


Terug naar het overzicht

 FAQ

ADDITIONAL LEVEL OF DRIERS BASED ON RESIGN SOLIDS:

Cobalt

0.06%

to

0.20%
Lead

0.50%

to

1.00%
Calcium

0.20%

to

0.40%
Zirconium

0.10%

to

0.50%
Barium

0.10%

to

0.50%
Manganese

0.20%

to

0.30%
Zinc

0.10%

to

0.50%
Iron

0.20%

to

0.50%
Lithium

0.30%

to

0.50%

CALCIUM OF DRIERS:

Wt. of drier required = Resin solids X % Metal required X Wt. Resin in Paints X 10

Per Kg of Paint

100

% Metal in drier

FACTORS AFFECTING DRYING TIME:

  • Very fine particle sized pigments may absorb driers out of the systems leading to extended drying
  • Excess Anti- Skinning agent will increase the drying time
  • Presence of water in system will increase the drying time.
  • Driers need time to mature in the systems so initial drying will be different to those obtained after storage.
  • High humidity tends to slow the drying time.
  • High air movements & higher temperature reduce the drying time.
  • Different test methods will give different results viz. Touch dry & tack free, BK drying time, Other methods 

STAGE OF ADDITION:

  • Unless being used as dispersing agent driers should be added at the end of the manufacturing Process & preferably after the paints has cooled to ambient temperature.
  • Addition of the Cobalt drier or combination driers containing Cobalt to the paint at high tempera­ture could cause discoloration or gellation. This also applies to manganese drier.
  • Ensure that the driers are completely incorporated into the paint. There should be no left over drier in the weighing vessel.
  • Do not pre mix driers & anti-skinning agent prior to addition to the paint.